Silicate
paint for mineral facades |
|
|
|
· Very good water vapor permeability |
·
Forms water repellent surface |
|
· Good
weather resistance |
|
· Easy
to clean |
|
|
|
Fields of
application |
Residential,
commercial, industrial buildings and storage facilities. Applicable for
painting concrete, lime- or lime-and-cement treated plaster surfaces,
silicate bricks, as well as for surfaces formerly painted with lime-,
lime-and-cement, cement or silicate paint. |
|
Can be used
also for interior mineral surfaces |
Gloss |
Full matt. |
Coverage (per
coat) |
3- 5 m2/l. Coverage depends on painting method and
roughness of the surface painted. |
Tinting |
The paint can
be used white (SA base) or tinted according to Tikkurila Facade and Hansa
Silicate colour cards (base SА and SC base). Tinted products cannot be
exchanged. |
Base paints |
SA and SC base. |
Application
method |
To be applied
with a painting brush, roller or high pressure airbrush. The high-pressure
airbrush nozzle shall be 0,018” - 0,023” or 0,460 - 0,580 mm. |
Drying time |
(at +23 °С, relative air humidity (RH) 50%) |
|
12 hours – recoatable. |
Cleaning of painting
tools, thinner |
Tools can be cleaned with water. Paint can be thinned
with Hansa Silicate Primer, use instructions below. |
Storage |
Protect the product from frost! |
Storage time |
In tightly closed original container 2 years from
production date (stated on can). |
Solid content |
About. 50% v/v. |
Density |
1,3- 1,4
kg/l, depending on the base paint and
shade (ISO 2811). |
Water vapour diffusion |
Sd, H2O≤0,14м, when applied according to manufacturer's
instructions (ISO 7783-2). |
Carbon dioxide diffusion resistance |
Sd, CO2 < 1m, when applied according to
manufacturer's instructions. |
Adhesion |
0,8 N/mm2 , when applied according to manufacturer's
instructions ( ISO 4624). |